Products

Products Categories

High Quality Corrosion Resistant Quartz Fiber N...

High Temperature Resistance Quartz Fiber Needle...

High Tensile Strength Customized Quartz Fiber N...

3-40mm Thick High Quality Quartz Fiber Needled ...

Custom Good Quality Quartz Fiber Fabric Cloth

Lightweight 100gsm 200gsm Quartz Fiber Fabric

High Temperature Resistance Quartz Fiber Cloth ...

High Quality Plain Twill Quartz Fiber Fabric

Good quality 300g Fiberglass Chopped Strand Mat

Hot Selling Good Quality Fiberglass Surface Tissue

12K 200g UD Carbon Fiber Cloth For Concrete Construction

Carbon fiber cloth is a high-strength, high modulus composite material widely used in aviation, automotive, sports equipment and other fields. In carbon fiber cloth, unidirectional and bidirectional are two common types of fiber cloth.
UD carbon fiber cloth refers to the arrangement of fibers in only one direction, that is, only longitudinal or transverse fibers. The unidirectional characteristic of carbon fiber cloth is that it has very high strength and stiffness, and can withstand a large amount of tensile and compressive forces. The unidirectional application of carbon fiber cloth is very extensive, and it can be used to make airplanes, cars, ships, sports equipment, and so on.

Min.Order: 50 square meters
Style: UD
Color: Black
Payment Type: T/T,Paypal,Credit card,L/C,Western Union
Transportation: Ocean,Land,Air,Express
Port: Shanghai,Guangdong,Qingdao

product details

product Parameter

Product Feature

UD carbon fiber fabric has extremely high strength and light weight, which makes it highly valuable in structural design. In addition, it also has excellent wear resistance and corrosion resistance, and can maintain stable performance even in harsh environments. More importantly, UD carbon fiber fabric has a low coefficient of thermal expansion and excellent fatigue resistance, which can effectively extend its service life and improve safety.

Product Information
Product Type	UD Carbon Fiber Fabric
Material	100% carbon fiber
Fabric Type	Cloth
Warp	12k
FAW	200g/m2
Thickness	0.111mm
Color	Black
Width	100cm or customized

More Choice

Application Field

Used for seismic reinforcement of beams in building structure reinforcement engineering. A certain bridge project uses UD carbon fiber cloth with specific requirements, which is pasted along the tension zone at the bottom of the beam, and combined with matching impregnated adhesive to form a composite material layer, which increases the bending bearing capacity of the beam by 40% and reduces the crack width from 0.3mm to 0.05mm.

Application of industrial equipment foundations reinforcement. Due to long-term corrosion, the bearing carrying of the reactor support in a certain chemical plant has decreased. Therefore, 200g/㎡ UD carbon fiber cloth is used for circumferential reinforcement. During construction, the fiber direction is perpendicular to the axial direction of the support, forming a 360 degree constraint to restore the compressive strength of the support to 120% of the design value.

Why Choose Us?

Buyer Review

Our Factory

Packing & Transportation

FAQ

Learn more

Product Parameter

Technical parameters of carbon fiber unidirectional fabric
Specification	Ⅰ		Ⅱ
Surface density	200 g/ m2	300 g/ m2	200 g/ m2	300 g/ m2
Theoretical thickness	0.111 mm	0.167 mm	0.111 mm	0.167 mm
Tensile strength	≥3400 MPa	≥3400 MPa	≥3000 MPa	≥3000 MPa
Elastic modulus	≥240 GPa	≥240 GPa	≥210 GPa	≥210 GPa
Breaking elongation	≥1.7%	≥1.7%	≥1.5%	≥1.5%